射出成形機重量の基本規格

射出重量

射出重量 is an important parameter of the injection molding machine. It is the most frequently used parameter when selecting an injection molding machine, expressed in ounces or grams. Although this parameter is simple and easy to understand, it is easy to be misunderstood. The reason is very simple. When the plastic is selected, the injection molder can determine the weight of the plastic part, so they can easily choose the machine by this injection weight. In fact, the injection weight is defined as the weight of the plastic injection when an empty injection (not injected into the mold) is measured, rather than theoretically calculated. The compound used is usually a general hard rubber with a specific gravity of 1.05. When the plastic of the plastic part is different from PS, the injection weight of the specification can be used after the following conversion. Injection weight of non-PS plastic = c*b/1.05, (b = specific gravity of plastic and c = injection weight expressed in PS.) For example: the specific gravity of Saigang is 1.42, it is in one injection weight (calculated as PS) 8 oz.

(1) 十分な射出重量を備えた射出成形機を選択します。プラスチック部品の重量と流路プラスチックの重量を足したものにちょうど等しい射出重量を備えた射出成形機を選択するべきではありません。おもちゃの肖像画など、それほど要求の厳しい射出成形では、総重量は射出重量の 85% である必要があります。クリスタルの供給など、要求の厳しい射出成形では 75%。空射出で測定される射出重量は射出圧力では小さく、高射出成形では高い射出圧力が必要となります。

たとえば、比重 1.38 の硬質ポリ塩化ビニル (UPVC) を使用しておもちゃの肖像画を成形する場合、プラスチック部品とランナー プラスチックの重さは 4 オンスであり、射出成形機で射出する必要があります。射出重量は PS = 4*1.05/0.38 =3.04 オンスで特徴付けられます。 85% ガイドを使用すると、必要な射出射出重量 = 3.04 / 0.85 = 3.58 オンスとなります。

(2) 過度の射出重量を有する射出成形機は使用しないでください。プラスチック部品とランナー プラスチックの総重量は、射出重量の 35% ～ 85% である必要があります。下限は、ステンシルの曲がり、バレル内のプラスチックの滞留時間、射出成形品の kg あたりの消費電力という 3 つの考慮事項によって決まります。

小さな射出成形部品に小さな金型を使用すると、テンプレートが過度に曲がってしまい、テンプレートに傷がついたり (製品の品質に影響を与える)、さらにはテンプレートが破断したりする可能性があります。

大型の射出成形機を使用して小さなプラスチック部品を射出成形すると、溶融物の滞留時間が長すぎるとプラスチックが分解してしまいます。

マルチキャビティまたはより大きな金型サイズを使用すると、大型機械で小さなプラスチック部品を成形する際の問題の一部を解決できます。バレルの温度を下げると、滞留時間が長いため音声の分解も緩和されます。